Magnus COMPREG Plywood for Mould & Die Casting is a technically precise product. The manufacturing and testing processes target creating a quality product with high chemical and mechanical standards. The raw materials like veneer, resin and other chemicals are screened for suitability. The timber is sourced from hardwood species like Gurjan (Dipterocarpus) Steam Beech (Fagus sylvatica). This is then steam treated for oil removal and fibre softening to ensure precision lathe peeling. The controlled curing process is designed to roll out a high quality grade product.

Suitable for: Moulds making for injection molding, blow molding, transfer molding rotational molding, casting, patterns, profiles, extrude, die and more.

Thickness: 25 to 200 mm

Size: 1220 x 120 to 1675 x 3200 mm

Density: 0.95 to 1.40 gm/cm3

Adhesive: BWP grade, IS 848:2006



Pin It
industrial compreg for mould die

industrial compreg for mould die

TECHNICAL SPECIFICATIONS
  Properties BIS Requirement IS 3513:1989 Observation Values
1. Length 2440mm 2442mm
2. Width 1220mm 1222mm
3. Thickness 35mm 35.15mm
4. Squareness 2 % 1mm
5. Edge straightness 2 % 0.95mm
6.

Density

0.95 to 1.25 gm/cm2 1.20 gm/cm2
7. Moisture content 6 to 12 % 7.50 %
  Physical properties
8 Tensile strength 59 Mpa 140 Mpa
9. Static bending MOR 59 Mpa 170 Mpa
10. Compressive strength parallel to laminate 75 Mpa 120 Mpa
11. Perpendicular to laminate 130 Mpa 170 Mpa
12. Hardness test hardness on rockwell H scale 60 65  
13. Impact strength parallel to laminate 0.5 kg-M/cm2 0.58 kg-M/cm2
14. Perpendicular to laminate 0.2 kg-M/cm2 0.29 kg-M/cm2
15. Thickness swelling (3% Max.)
within 4 hrs.
water soaking with in 4 hrs.

0.40% Max.
1.50% Max.